108552
论文已发表
注册即可获取德孚的最新动态
IF 收录期刊
- 3.4 Breast Cancer (Dove Med Press)
- 3.2 Clin Epidemiol
- 2.6 Cancer Manag Res
- 2.9 Infect Drug Resist
- 3.7 Clin Interv Aging
- 5.1 Drug Des Dev Ther
- 3.1 Int J Chronic Obstr
- 6.6 Int J Nanomed
- 2.6 Int J Women's Health
- 2.9 Neuropsych Dis Treat
- 2.8 OncoTargets Ther
- 2.0 Patient Prefer Adher
- 2.2 Ther Clin Risk Manag
- 2.5 J Pain Res
- 3.0 Diabet Metab Synd Ob
- 3.2 Psychol Res Behav Ma
- 3.4 Nat Sci Sleep
- 1.8 Pharmgenomics Pers Med
- 2.0 Risk Manag Healthc Policy
- 4.1 J Inflamm Res
- 2.0 Int J Gen Med
- 3.4 J Hepatocell Carcinoma
- 3.0 J Asthma Allergy
- 2.2 Clin Cosmet Investig Dermatol
- 2.4 J Multidiscip Healthc
已发表论文
钙硅基大孔径介孔生物活性材料用于成骨性能研究
Authors Zeng D, Zhang X, Wang X, Cao L, Zheng A, Du J, Li Y, Huang Q, Jiang X
Received 21 June 2017
Accepted for publication 26 September 2017
Published 15 November 2017 Volume 2017:12 Pages 8277—8287
DOI https://doi.org/10.2147/IJN.S144528
Checked for plagiarism Yes
Review by Single-blind
Peer reviewers approved by Dr Govarthanan Muthusamy
Peer reviewer comments 2
Editor who approved publication: Dr Linlin Sun
摘要：我们前期的研究发现，钙硅基介孔材料溶解离子在其表面可以形成一层碳酸羟基磷灰石，具有良好的骨传导性。然而，钙硅基介孔材料的骨再生生物学机制还需进一步探讨。本研究的主要目的是通过碱性磷酸酶检测，实时荧光定量 PCR 分析、von Kossa 和茜素红染色等方法评估大孔径介孔钙硅基生物陶瓷（LPMSCs）的成骨能力。实验结果表明，与大孔径介孔二氧化硅相比（LPMS），LPMSCs 曾对牙髓细胞的成骨分化效果更好好。LPMSC-2 和 LPMSC-3 钙含量更高，其成骨能力也比 LPMSC-1 更好，而这可能与钙敏感受体通路相关。此外，体外负载和缓释实验表明，与 LPSC 相比，改性后的 LPMSCs 对重组人血小板源性生长因子（rhPDGF-BB）也有较好的负载能力和缓释速率。动物颅骨缺损修复结果表明，LPMSC-2 和 LPMSC-3 的新骨形成量多于 LPMSC-1 和 LPSC。由此可知，LPMSC-1 具有良好的成骨能力和较好的生长因子承载能力，这可能是由于其适度的 Ca /硅摩尔比。
Keywords: mesoporous Ca-Si-based materials, dental pulp cells, rat calvarial defect
Keywords: mesoporous Ca-Si-based materials, dental pulp cells, rat calvarial defect